Note publique d'information : LES PROPRIETES TRIBOLOGIQUES DE L'ACIER AUSTENITIQUE 304L SONT CONSIDERABLEMENT AMELIOREES
LORSQUE L'ON REALISE, PAR TECHNIQUES DE FAISCEAUX D'IONS, UN REVETEMENT CRISTALLIN
MINCE D'ALLIAGES A BASE DE NICKEL. TOUTEFOIS, L'AMELIORATION DEPEND FORTEMENT DES
PARAMETRES D'ELABORATION QUI GOUVERNENT LA MICROSTRUCTURE DES DEPOTS. LES REVETEMENTS
ELABORES PAR SIMPLE PULVERISATION D'UNE CIBLE DE NI AVEC N#+ ONT LA STRUCTURE DE NI#3N;
LES PROPRIETES TRIBOLOGIQUES DE L'ENSEMBLE DEPOT/SUBSTRAT SONT MOYENNES. L'IMPLANTATION
D'IONS AR#+ PENDANT LE DEPOT CONDUIT A UNE STRUCTURE BIPHASEE A PETITS GRAINS, CONSTITUEE
DE NI ET NI#4N (OU A LA STRUCTURE DE NI SEUL SI L'ION PULVERISATEUR EST AR#+), AVEC
UNE ORIENTATION PREFERENTIELLE DES PLANS (111) PARALLELEMENT A LA SURFACE DE L'ECHANTILLON;
LES PERFORMANCES TRIBOLOGIQUES DE L'ENSEMBLE DEPOT/SUBSTRAT SONT PARMI LES MEILLEURES
OBTENUES DANS CETTE ETUDE. LES REVETEMENTS ELABORES PAR PULVERISATION D'UNE CIBLE
DE NITI AVEC AR#+ ONT UNE STRUCTURE AMORPHE NITI ET PRESENTENT DE MAUVAISES PROPRIETES
TRIBOLOGIQUES. LORSQUE LE GAZ PULVERISATEUR CONTIENT AU MOINS 50% D'AZOTE, LES DEPOTS
ONT UNE STRUCTURE BIPHASEE CONSTITUEE D'UNE PHASE MAL CRISTALLISEE NI#3N ET D'UNE
PHASE DURE TIN; LES PERFORMANCES TRIBOLOGIQUES SONT BONNES. LES MEILLEURS RESULTATS
SONT OBTENUS QUAND IL Y A ASSISTANCE IONIQUE ET CHAUFFAGE PENDANT LE DEPOT, MAIS ALORS
LA STRUCTURE DES COUCHES EST CONSTITUEE D'UNE PHASE NI ASSOCIEE A LA PHASE TIN. L'IMPLANTATION
IONIQUE AMELIORE LES PROPRIETES TRIBOLOGIQUES DES REVETEMENTS; CECI SEMBLE ETRE LE
RESULTAT D'UNE DENSIFICATION DU DEPOT QUI EST REVELEE PAR L'AUGMENTATION IMPORTANTE
DE LA DURETE, ET PEUT S'EXPLIQUER PAR LA GRANDE MOBILITE ATOMIQUE DUE AUX DEFAUTS
EN SURSATURATION. TOUS LES REVETEMENTS CRISTALLINS ETUDIES SONT GENERALEMENT FRAGILES
ET PRESENTENT, PAR SUITE, UNE ADHERENCE MOYENNE SUR L'ACIER 304L RELATIVEMENT MOU;
ON PEUT PENSER QUE LES AMELIORATIONS TRIBOLOGIQUES SERAIENT AMPLIFIEES AVEC UN SUBSTRAT
PLUS DUR. LES PROPRIETES TRIBOLOGIQUES DES REVETEMENTS CONTENANT LA PHASE NI SONT
MEILLEURES QUE CELLES DU NICKEL MASSIF; CECI EST PROBABLEMENT DU A LA TRES FAIBLE
GROSSEUR DE GRAINS DES DEPOTS ET, SOUS ASSISTANCE D'IONS, A L'ORIENTATION PREFERENTIELLE
DES PLANS (111) DU NICKEL PARALLELEMENT A LA SURFACE DU SUBSTRAT