Note publique d'information : LES DICHALCOGENURES DE METAUX REFRACTAIRES SONT DES COMPOSES DONT LES PROPRIETES CHIMIQUES
ET PHOTOELECTRIQUES SONT SUSCEPTIBLES D'APPLICATIONS DANS LE DOMAINE DE LA CONVERSION
D'ENERGIE PHOTOELECTROCHIMIQUE. LE WSE#2, DE PART LA VALEUR DE SA BANDE INTERDITE
(1.35 EV) EST L'UN DES PLUS PROMETTEURS DE CES COMPOSES. L'OBJET DE CE TRAVAIL A ETE
DE METTRE AU POINT DES TECHNIQUES D'OBTENTION DE CE MATERIAU. A CETTE FIN LES MONTAGES
DE DEPOT UTILISES ONT ETE OPTIMISES DE FACON A OBTENIR LES COUCHES DESIREES. CELLES-CI
ONT ETE CARACTERISEES PAR DIFFRACTION DE RAYONS X, MICROSCOPIE A BALAYAGE ET A TRANSMISSION,
MICROSONDE-ELECTRONIQUE, SPECTROSCOPIE DE PHOTOELECTRONS (XPS), ABSORPTION OPTIQUE
ET MESURE DE LA VARIATION DE LA CONDUCTIVITE EN FONCTION DE LA TEMPERATURE. DANS LE
CAS DE COUCHES MINCES DE WSE#2, CE COMPOSE A PU ETRE OBTENU PAR SIMPLE SYNTHESE A
PARTIR D'UNE PLAQUE DE TUNGSTENE ET D'UN GRAIN DE SELENIUM, LE TOUT ETANT RECUIT DANS
UN TUBE SCELLE SOUS VIDE. CEPENDANT L'ADHERENCE DES COUCHES AU SUBSTRAT DE TUNGSTENE
EST FAIBLE. C'EST POURQUOI UNE AUTRE TECHNIQUE A ETE UTILISEE A SAVOIR, DEPOT DE FEUILLET
SUPERPOSE W/SE/W...W SUIVI D'UN TRAITEMENT THERMIQUE, QUI PERMET, PAR REACTION CHIMIQUE
A L'ETAT SOLIDE, LA FORMATION DE COUCHES MINCES DE WSE#2. LES CONDITIONS DU TRAITEMENT
THERMIQUE ONT ETE OPTIMISEES DE FACON A OBTENIR DES COUCHES CONTINUES ET TEXTUREES
DE TELLE MANIERE QUE L'AXE C DES CRISTALLITES SOIT PERPENDICULAIRE AU PLAN DU SUBSTRAT.
LES MESURES DE CONDUCTIVITE MONTRENT CEPENDANT QUE CELLE-CI EST CONTROLEE PAR LES
JOINTS DE GRAINS. CECI EST CONFIRME PAR LA MICROSCOPIE ELECTRONIQUE A TRANSMISSION
QUI MONTRE QUE LA CONTINUITE ENTRE LES CRISTALLITES ORIENTES ET ASSUREE PAR DES MICROCRISTALLITES
DESORDONNES. PARALLELEMENT A L'ETUDE DU WSE#2, DES COUCHES DE CUINSE#2 ONT ETE REALISEES
DE FACON A GENERALISER LA TECHNIQUE D'OBTENTION MISE AU POINT POUR LE WSE#2. LES FEUILLETS
DE CU, IN, SE SONT EVAPORES SEQUENTIELLEMENT DANS LE RAPPORT STCHIOMETRIQUE DESIRE.
UN RECUIT A 623K PENDANT 3H PERMET D'OBTENIR DU CUINSE#2 CRISTALLISE DANS LA STRUCTURE
CHALCOPYRITE. LE CONTACT MO/CUINSE#2, SOUVENT UTILISE DANS LES STRUCTURES A BASE DE
CUINSE#2 A ETE ETUDIE EN TRACANT DES PROFILS XPS. ON MONTRE QUE SE DIFFUSE DANS MO
AVEC FORMATION DE MOSE#2 A L'INTERFACE