Note publique d'information : AU COURS DE SON REFROIDISSEMENT, DE LA TEMPERATURE DU SOLIDUS A LA TEMPERATURE AMBIANTE,
LA FONTE A GRAPHITE SPHEROIDAL FERRITIQUE SUBIT UNE TRANSFORMATION DE PHASE. CETTE
DERNIERE LUI ATTRIBUE UN COMPORTEMENT COMPLEXE FAISANT APPARAITRE DES INTERDEPENDANCES
ENTRE LA REPONSE MECANIQUE, LA REPONSE THERMIQUE ET LE CHANGEMENT MICROSTRUCTURAL.
EN PARTICULIER, L'INFLUENCE DE L'EVOLUTION DE LA MICROSTRUCTURE SUR LE COMPORTEMENT
MECANIQUE SE TRADUIT PAR NON SEULEMENT DES MODIFICATIONS DES CARACTERISTIQUES MECANIQUES
MAIS AUSSI L'APPARITION D'AUTRES PHENOMENES TELS QUE LA PLASTICITE DE TRANSFORMATION
DE PHASE ET LA DILATATION THERMO-METALLURGIQUE DUE A LA VARIATION VOLUMIQUE AU COURS
DU CHANGEMENT MICROSTRUCTURAL. HORS DU DOMAINE DU CHANGEMENT DE PHASE, LE MATERIAU
ETANT FORME D'UNE SEULE PHASE, NOUS NOUS PROPOSONS DE MODELISER SON COMPORTEMENT PAR
UN MODELE ELASTO-VISCOPLASTIQUE ANISOTHERME BASE SUR LA THERMODYNAMIQUE DES PROCESSUS
IRREVERSIBLES AVEC VARIABLES INTERNES. QUANT A LA DESCRIPTION DU COMPORTEMENT DU MATERIAU
BIPHASIQUE AU COURS DE LA TRANSFORMATION DE PHASE, ELLE EST BASEE SUR LA THEORIE DES
MELANGES AVEC UNE APPROCHES SIMPLIFIEE QUI CONSISTE A PRENDRE LA DEFORMATION TOTALE
ET LA TEMPERATURE COMME VARIABLE COMMUNE AUX DEUX PHASES PRESENTES DANS LE MATERIAU
(MODELE DE VOIGT). PAR AILLEURS, POUR MODELISER LE CHANGEMENT DE PHASE UNE VARIABLE
INTERNE SUPPLEMENTAIRE EST INTRODUITE. ELLE REPRESENTE LA FRACTION VOLUMIQUE DE LA
PHASE NAISSANTE. L'UTILISATION DES COUPLAGES D'ETAT, DE DISSIPATION ET D'EVOLUTION
PERMETTENT, QUANT A EUX, DE TENIR COMPTE DES INTERACTIONS QUI EXISTENT ENTRE LES DIFFERENTS
MECANISMES MIS EN JEU DANS LE COMPORTEMENT DE LA FONTE ETUDIEE ET AINSI DE PRECISER
LA FORME DE CHACUN DES POTENTIELS THERMODYNAMIQUES ET DE DISSIPATION. LES LOIS DE
COMPORTEMENT, QUI EN DECOULENT, PERMETTENT LA DESCRIPTION DU COMPORTEMENT ELASTO-VISCOPLASTIQUE
ANISOTHERME DU MATERIAU AVEC PRISE EN COMPTE DE LA TRANSFORMATION DE PHASE. POUR IDENTIFIER
LES PARAMETRES DE LA LOI PROPOSEE, NOUS AVONS EFFECTUE UNE IMPORTANTE CAMPAGNE D'ESSAIS
ISOTHERMES ET ANISOTHERMES (TRACTION, FLUAGE, RELAXATION, DILATATION, RESISTIVITE...).
UNE COMPARAISON ENTRE LES ESSAIS DE VERIFICATION ET LE MODELE EST EFFECTUEE OU L'ON
NOTE UNE BONNE PREVISION DU MODELE POUR L'ENSEMBLE DES PHENOMENES PRIS EN COMPTE